Effect of different materials for conventional and 3D-printed models on the mechanical properties of ethylene-vinyl acetate utilized for fabricating custom-fit mouthguards.

BACKGROUND/AIM: The interaction between the ethylene-vinyl acetate (EVA) with distinct materials utilized for obtaining dental models can affect the performance of resulting mouthguards. This study attempted to evaluate the effect of different materials for conventional (dental stone) or 3D-printed (resin) models on EVA's physical and mechanical properties and surface characteristics. MATERIAL AND METHODS: EVA sheets (Bioart) were laminated over four model types: GIV, conventional Type IV dental stone model (Zhermak); ReG, resin-reinforced Type IV dental stone model (Zero Stone); 3DnT, 3D resin printed model (Anycubic) without surface treatment; 3DT, 3D-printed model (Anycubic) with water-soluble gel (KY Jelly Lubricant, Johnson & Johnson) coating during post-curing process. The EVA specimens were cut following the ISO 37-II standard (n = 30). Shore A hardness was measured before and after plasticization on the contact (internal) or opposite (external) surfaces with the model. The breaking force (F, N), elongation (EL, mm), and ultimate tensile strength (UTS, MPa) were measured using a universal testing machine. Macro-photography and scanning electron microscopy were adopted for classifying the EVA surface alteration. Data were analyzed by one-way ANOVA with repeated measures, followed by Tukey's test (α = .05). RESULTS: Plasticization significantly decreased Shore A values for the tested EVA regardless of the model type (p < .001). Higher F, El, and UTS values were verified for the EVA with 3DT and GIV models compared to ReG and 3DnT (p < .001). 3DnT models resulted in severe surface alteration and a greater reduction of the mechanical properties of the EVA. CONCLUSION: The interaction of EVA with 3D resin-printed models without surface treatment or resin-reinforced Type IV dental stone models significantly affected the physical and mechanical properties of this material. The utilization of water-soluble gel coating during the post-curing process of 3D resin printed models improved the mechanical properties of the EVA, similarly when this material was plasticized over conventional Type IV dental stone model.

Influence of carbonated acid beverage on fracture resistance and marginal gap formation in different restorative approaches to non-carious cervical lesions.

OBJECTIVE: This study is to evaluate fracture resistance, failure mode, and gap formation at the restorative interface of unrestored or restored non-carious cervical lesions (NCCLs) submitted to a short-term erosive environment. MATERIALS AND METHODS: Artificial NCCLs were produced in vitro in bovine incisors, and were randomly divided into four restorative resins groups (n = 22): nanohybrid-NR; bulk-fill-BR; flow with a nanohybrid layer-FNR; bulk-fill with a nanohybrid layer-BNR; and a group unrestored-UR (n = 16). Half of the specimens were submitted to an erosive challenge (per 5 min, 3 × a day for 7 days, before and after restoration), and the other half, was immersed in artificial saliva. After, all teeth undergone thermal (5 ºC, 37 ºC, and 55 ºC, 3600 cycles) and mechanical (50 N, 2 Hz, 300,000 cycles) aging. Eighty teeth were subjected to compressive loading, and resistance and failures were analyzed, while 24 teeth were evaluated for gaps by microcomputed tomography. Statistical tests were performed (p < 0.05). RESULTS: The restorative approaches affected fracture resistance (η2p = 0.14, p = 0.023), and gap formation (η2 = 0.18, p = 0.012) and so did the immersion medium (fracture η2p = 0.09, p = 0.008; gap η2 = 0.09, p = 0.017). BNR showed the highest resistance, while UR the lowest. FNR showed the highest gaps in both immersion media. Neither the resin groups nor the immersion media were associated with failure mode. CONCLUSIONS: The erosive immersion medium based in acid beverages has been shown to affect NCCLs with or without restoration, but when Bulk-Fill resin is covered by nanohybrid resin, the performance is good. CLINICAL RELEVANCE: Erosion negatively affects restorations, but unrestored NCCL shows worse biomechanical performance in stress-bearing situations.

Influence of Tip Diameter and Light Spectrum of Curing Units on the Properties of Bulk-Fill Resin Composites.

OBJECTIVE: The aim of this study was to evaluate the influence of different light-curing units (LCUs) with distinct tip diameters and light spectra for activating bulk-fill resins. MATERIALS AND METHODS: The specimens (n = 10) were made from a conventional composite (Amaris, VOCO) and bulk-fill resins (Aura Bulk Fill, SDI; Filtek One, 3M ESPE; Tetric Bulk Fill, Ivoclar Vivadent) with two diameters, 7 or 10 mm, × 2 mm thickness. Following 24 hours of specimen preparation, the degree of conversion (DC) was evaluated using the Fourier-transform infrared unit. Knoop hardness (KHN) readings were performed on the center and periphery of the specimens. Data were assessed for homoscedasticity and submitted to one-way and three-way analysis of variance followed by the Tukey's and Dunnett's tests, depending on the analysis performed (α = 0.05). RESULTS: LCUs and specimen diameter significantly affected the DC. The Tetric Bulk Fill provided increased DC results when light-cured with Valo (54.8 and 53.5%, for 7 and 10 mm, respectively) compared with Radii Xpert (52.1 and 52.9%, for 7 and 10 mm, respectively). No significant differences in KHN results were noted for the conventional resin composite (Amaris) compared with LCUs (p = 0.213) or disc diameters (p = 0.587), but the center of the specimen exhibited superior KHN (p ≤ 0.001) than the periphery. CONCLUSION: The light spectrum of the multipeak LCU (Valo) significantly increased the DC and KHN of the bulk-fill resin composite with additional initiator to camphorquinone (Tetric Bulk Fill) compared with the monowave LCU (Radii Xpert). The tip size of the LCUs influenced the performance of some of the resin composites tested.

Microstructural and mechanical analysis of two CAD-CAM lithium disilicate glass-reinforced ceramics.

The aim of this study was to analyze the structural, morphological and mechanical properties of two different lithium disilicate glass-reinforced ceramics for CAD-CAM systems (IPS e.max CAD and Rosetta SM). Five methodologies were used for both ceramics: microstructure (n = 2) was analyzed using x-ray diffraction (XRD); morphological properties (n = 2) were analyzed by scanning electron microscopy (SEM), with and without hydrofluoric etching; porosity (n = 3) was assessed using 3D micro-computed tomography (micro-CT); flexural strength was measured (n =1 0) using the three-point bending test; and bond strength was determined with self-adhesive resin cement (n = 10), using a microshear bond test. After performing all the tests, the data were analyzed using t-Student test and two-way ANOVA. All the tests used a significance level of α = 0.05. High peak positions corresponding to standard lithium metasilicate and lithium disilicate with similar intensities were observed for both ceramics in the XRD analysis. Morphological analysis showed that the crystalline structure of the two ceramics studied showed no statistical difference after acid etching. Additionally, no significant differences were recorded in the number or size of the pores for the ceramics evaluated. Moreover, no differences in flexural strength were found for the ceramic materials tested, or in the bond strength to ceramic substrates for the resin cements. Based on the study results, no significant differences were found between the two CAD-CAM lithium disilicate glass-reinforced ceramics tested, since they presented similar crystalline structures with comparable intensities, and similar total porosity, flexural strength and bond strength.

Microstructural and mechanical analysis of two CAD-CAM lithium disilicate glass-reinforced ceramics

Abstract The aim of this study was to analyze the structural, morphological and mechanical properties of two different lithium disilicate glass-reinforced ceramics for CAD-CAM systems (IPS e.max CAD and Rosetta SM). Five methodologies were used for both ceramics: microstructure (n = 2) was analyzed using x-ray diffraction (XRD); morphological properties (n = 2) were analyzed by scanning electron microscopy (SEM), with and without hydrofluoric etching; porosity (n = 3) was assessed using 3D micro-computed tomography (micro-CT); flexural strength was measured (n =1 0) using the three-point bending test; and bond strength was determined with self-adhesive resin cement (n = 10), using a microshear bond test. After performing all the tests, the data were analyzed using t-Student test and two-way ANOVA. All the tests used a significance level of α = 0.05. High peak positions corresponding to standard lithium metasilicate and lithium disilicate with similar intensities were observed for both ceramics in the XRD analysis. Morphological analysis showed that the crystalline structure of the two ceramics studied showed no statistical difference after acid etching. Additionally, no significant differences were recorded in the number or size of the pores for the ceramics evaluated. Moreover, no differences in flexural strength were found for the ceramic materials tested, or in the bond strength to ceramic substrates for the resin cements. Based on the study results, no significant differences were found between the two CAD-CAM lithium disilicate glass-reinforced ceramics tested, since they presented similar crystalline structures with comparable intensities, and similar total porosity, flexural strength and bond strength.

Influence of Hemostatic Solution on Bond Strength and Physicochemical Properties of Resin Cement.

The aim of this study was to evaluate the degree of conversion, color stability, chemical composition, and bond strength of a light-cured resin cement contaminated with three different hemostatic solutions. Specimens were prepared for the control (uncontaminated resin cement) and experimental groups (resin cement contaminated with one of the hemostatic solutions) according to the tests. For degree of conversion, DC (n = 5) and color analyses (n = 10), specimens (3 mm in diameter and 2 mm thick) were evaluated by Fourier transform infrared spectroscopy (FTIR) and CIELAB spectrophotometry (L*, a*, b*), respectively. For elemental chemical analysis (n = 1), specimens (2 mm thick and 6 mm in diameter) were evaluated by x-ray energy-dispersive spectroscopy (EDS). The bond strengths of the groups were assessed by the microshear test (n = 20) in a leucite-reinforced glass ceramic substrate, followed by failure mode analysis by scanning electron microscopy (SEM). The mean values, except for the elemental chemical evaluation and failure mode, were evaluated by ANOVA and Tukey's HSD test. The color stability was influenced by storage time (p<0.001) and interaction between contamination and storage time (p<0.001). Hemostop and Viscostat Clear contamination did not affect the DC, however Viscostat increased the DC. Bond strength of the resin cement to ceramic was negatively affected by the contaminants (p<0.001). Contamination by hemostatic agents affected the bond strength, degree of conversion, and color stability of the light-cured resin cement tested.

Analysis of the presence of filling material in oval root canals using computed microtomography after endodontic retreatment performed by different techniques

The aim of this study was to evaluate the presence of filling material in oval root canals after endodontic retreatment performed by different techniques, considering the area (mm2), location and root third using computed microtomography (µ-CT). Methods: Thirty human lower central incisor underwent biomechanical preparation, root filling and filling removal using two techniques (n=15): MN- manual retreatment technique (Gates Glidden burs and stainless steel manual files); and RT- rotary retreatment technique (ProTaper Universal and ProTaper Retreatment Systems). Cross-sectional images of the teeth were made using µ-CT to identify the presence of remaining filling in all root thirds of the canal walls. The remaining material detected in 150 µ-CT sections was identified and its area quantified (mm2) for each root third individually. Results: Data analysis showed no difference in the remaining area of filling material (p=0.8611) for the both techniques. Higher frequency of remaining material was verified in the lingual wall of the root canals. Regardless of the retreatment technique, the apical third showed lager areas of remaining filling material. More areas of remaining material were detected in the cervical third of the RT group, whereas for the MN group, most areas were observed in the middle and apical thirds. Conclusion: According to our results, no significant differences were verified between the efficiency of the rotary and manual techniques for removing filling material due to the interferences caused by the root canal anatomy (AU)

Influence of Hemostatic Solution on Bond Strength and Physicochemical Properties of Resin Cement

Abstract The aim of this study was to evaluate the degree of conversion, color stability, chemical composition, and bond strength of a light-cured resin cement contaminated with three different hemostatic solutions. Specimens were prepared for the control (uncontaminated resin cement) and experimental groups (resin cement contaminated with one of the hemostatic solutions) according to the tests. For degree of conversion, DC (n = 5) and color analyses (n = 10), specimens (3 mm in diameter and 2 mm thick) were evaluated by Fourier transform infrared spectroscopy (FTIR) and CIELAB spectrophotometry (L*, a*, b*), respectively. For elemental chemical analysis (n = 1), specimens (2 mm thick and 6 mm in diameter) were evaluated by x-ray energy-dispersive spectroscopy (EDS). The bond strengths of the groups were assessed by the microshear test (n = 20) in a leucite-reinforced glass ceramic substrate, followed by failure mode analysis by scanning electron microscopy (SEM). The mean values, except for the elemental chemical evaluation and failure mode, were evaluated by ANOVA and Tukey's HSD test. The color stability was influenced by storage time (p<0.001) and interaction between contamination and storage time (p<0.001). Hemostop and Viscostat Clear contamination did not affect the DC, however Viscostat increased the DC. Bond strength of the resin cement to ceramic was negatively affected by the contaminants (p<0.001). Contamination by hemostatic agents affected the bond strength, degree of conversion, and color stability of the light-cured resin cement tested.

Resumo O objetivo desse estudo foi avaliar o grau de conversão, estabilidade de cor, composição química e resistência de união de um cimento resinoso fotoativado contaminado com três soluções hemostáticas diferentes. Foram preparadas amostras para o grupo controle (cimento não contaminado) e grupos experimentais (cimento contaminado com uma das soluções hemostáticas) de acordo com os testes. Para o grau de conversão e análise de cor (n=10), as amostras (3 mm de diâmetro e 2 mm de espessura) foram avaliadas por espectroscopia de infravermelho com transformação de Fourier (FTIR) e espectrofotometria CIELAB (L*, A*, B*), respectivamente. Para a análise química elementar (n=1), os espécimes (2 mm de espessura e 6 mm de diâmetro) foram avaliados por espectroscopia de energia dispersiva de raios-x (EDS). As resistências de união dos grupos foram avaliadas pelo ensaio de microcisalhamento (n=20) em um substrato cerâmico de vidro reforçado com leucita, seguida da análise de modo de falha por microscopia eletrônica de varredura (MEV). Os valores médios, com exceção da avaliação química e do modo de falha, foram avaliados por ANOVA e pelo teste de Tukey. A estabilidade de cor foi influenciada pelo tempo de armazenagem (p<0,001) e interação entre a contaminação e o tempo (p<0,001). A contaminação pelo Hemostop e Viscostat Clear não influenciaram no GC, porém a contaminação com Viscostat aumentou o GC. A resistência de união do cimento a cerâmica foi negativamente afetada pelos contaminantes (p<0,001). A contaminação por agentes hemostáticos afetou a resistência de união, o grau de conversão e a estabilidade de cor do cimento resinoso fotoativado testado.

Influence of Different Dentin Substrate (Caries-Affected, Caries-Infected, Sound) on Long-Term µTBS.

The aim of this study was to evaluate the µTBS in different dentin substrates and water-storage periods. Twenty-four dentin blocks obtained from sound third molars were randomly divided into 3 groups: Sound dentin (Sd), Caries-affected dentin (Ca) and Caries-infected dentin (Ci). Dentin blocks from Ca and Ci groups were subjected to artificial caries development (S. mutans biofilm). The softest carious tissue was removed using spherical drills under visual inspection with Caries Detector solution (Ca group). It was considered as Ci (softer and deeply red stained dentin) and Ca (harder and slightly red stained dentin). The Adper Single Bond 2 adhesive system was applied and Z350 composite blocks were built in all groups. Teeth were stored in deionized water for 24 h at 37 ºC and sectioned into beams (1.0 mm2 section area). The beams from each tooth were randomly divided into three storages periods: 24 h, 6 months or 1 year. Specimens were submitted to µTBS using EZ test machine at a crosshead speed of 1.0 mm/min. Failure mode was examined by SEM. Data from µTBS were submitted to split plot two-way ANOVA and Tukey's HSD tests (a=0.05). The µTBS (MPa) of Sd (41.2) was significantly higher than Ca (32.4) and Ci (27.2), regardless of storage. Ca and Ci after 6 months and 1 year, presented similar µTBS. Mixed and adhesive failures predominated in all groups. The highest µTBS values (48.1±9.1) were found for Sd at 24 h storage. Storage of specimens decreased the µTBS values for all conditions.

Degree of conversion and bond strength of resin-cements to feldspathic ceramic using different curing modes.

OBJECTIVE: The aim of this study was to assess the performance of resin cements when different curing modes are used, by evaluating the degree of conversion and bond strength to a ceramic substrate. MATERIAL AND METHODS: Three resin cements were evaluated, two dual-cured (Variolink II and RelyX ARC) and one light-cured (Variolink Veneer). The dual-cured resin cements were tested by using the dual activation mode (base and catalyst) and light-activation mode (base paste only). For degree of conversion (DC) (n=5), a 1.0 mm thick feldspathic ceramic disc was placed over the resin cement specimens and the set was light activated with a QTH unit. After 24 h storage, the DC was measured with Fourier transform infrared spectroscopy (FTIR). For microshear bond strength testing, five feldspathic ceramic discs were submitted to surface treatment, and three cylindrical resin cement specimens were bonded to each ceramic surface according to the experimental groups. After 24 h, microshear bond testing was performed at 0.5 mm/min crosshead speed until the failure. Data were submitted to one-way ANOVA followed by Tukey test (p<0.05). Scanning electron microscopy (SEM) was used for classifying the failure modes. RESULTS: Higher DC and bond strength values were shown by the resin cements cured by using the dual activation mode. The Variolink II group presented higher DC and bond strength values when using light-activation only when compared with the Variolink Veneer group. CONCLUSION: The base paste of dual-cured resin cements in light-activation mode can be used for bonding translucent ceramic restorations of up to or less than 1.0 mm thick.

Influence of Different Dentin Substrate (Caries-Affected, Caries-Infected, Sound) on Long-Term muTBS

Abstract The aim of this study was to evaluate the μTBS in different dentin substrates and water-storage periods. Twenty-four dentin blocks obtained from sound third molars were randomly divided into 3 groups: Sound dentin (Sd), Caries-affected dentin (Ca) and Caries-infected dentin (Ci). Dentin blocks from Ca and Ci groups were subjected to artificial caries development (S. mutans biofilm). The softest carious tissue was removed using spherical drills under visual inspection with Caries Detector solution (Ca group). It was considered as Ci (softer and deeply red stained dentin) and Ca (harder and slightly red stained dentin). The Adper Single Bond 2 adhesive system was applied and Z350 composite blocks were built in all groups. Teeth were stored in deionized water for 24 h at 37 ºC and sectioned into beams (1.0 mm2 section area). The beams from each tooth were randomly divided into three storages periods: 24 h, 6 months or 1 year. Specimens were submitted to µTBS using EZ test machine at a crosshead speed of 1.0 mm/min. Failure mode was examined by SEM. Data from µTBS were submitted to split plot two-way ANOVA and Tukey’s HSD tests (a=0.05). The µTBS (MPa) of Sd (41.2) was significantly higher than Ca (32.4) and Ci (27.2), regardless of storage. Ca and Ci after 6 months and 1 year, presented similar µTBS. Mixed and adhesive failures predominated in all groups. The highest µTBS values (48.1±9.1) were found for Sd at 24 h storage. Storage of specimens decreased the µTBS values for all conditions.

Resumo O objetivo neste estudo foi avaliar a resistência de união à microtração (RUµT) de um sistema adesivo convencional (Adper Single Bond 2 - SB) em diferentes substratos dentinários e períodos de armazenagem. Vinte e quatro blocos de dentina foram obtidos de terceiros molares hígidos e separados aleatoriamente em 3 grupos (n=8): dentina sadia (Ds), dentina afetada (Da) e dentina infectada (Di). A Da e a Di foram submetidas ao desenvolvimento biológico artificial de cárie (S. mutans). O tecido cariado amolecido foi removido usando broca esférica sob inspeção visual com a solução Caries Detector (grupo Da). Considerou-se como Di a dentina amolecida e fortemente pigmentada de vermelho e como Da, a dentina hígida e levemente pigmentada de vermelho. O sistema adesivo SB foi aplicado de acordo com as recomendações do fabricante e blocos da resina composta Z350 foram construídos (6 mm de altura). O conjunto (dente/bloco de resina) foi armazenado em água deionizada por 24 horas a 37 °C. Estes foram seccionados em palitos (1,0 mm2 de área), que foram separados aleatoriamente em 3 períodos de armazenagem: 24 horas, 6 meses e 1 ano. Os palitos foram submetidos ao ensaio de resistência de união à microtração na máquina EZ teste a uma velocidade de 1,0 mm/min. Dados de RUµT foram submetidos à Análise de Variância 2 fatores em esquema de parcela subdividida e ao teste de Tukey (a=0,05). Os valores de resistência (MPa) da Ds (41,2) foram significativamente maiores do que os da Da (32,4) e Di (27,2), independente do tempo de armazenagem. Di e Da, 6 meses e 1ano, apresentaram valores similares de resistência de união. As falhas adesivas e mistas foram predominantes para todos os grupos. Em conclusão, os maiores valores de RUµT (48,1±9,1) foram verificados para a Ds e 24 h de armazenagem. A armazenagem diminuiu os valores de RUµT para todas as condições.

Degree of conversion and bond strength of resin-cements to feldspathic ceramic using different curing modes

Abstract Resin cements have led to great advances in dental ceramic restoration techniques because of their ability to bond to both dental structures and restorative materials. Objective The aim of this study was to assess the performance of resin cements when different curing modes are used, by evaluating the degree of conversion and bond strength to a ceramic substrate. Material and Methods Three resin cements were evaluated, two dual-cured (Variolink II and RelyX ARC) and one light-cured (Variolink Veneer). The dual-cured resin cements were tested by using the dual activation mode (base and catalyst) and light-activation mode (base paste only). For degree of conversion (DC) (n=5), a 1.0 mm thick feldspathic ceramic disc was placed over the resin cement specimens and the set was light activated with a QTH unit. After 24 h storage, the DC was measured with Fourier transform infrared spectroscopy (FTIR). For microshear bond strength testing, five feldspathic ceramic discs were submitted to surface treatment, and three cylindrical resin cement specimens were bonded to each ceramic surface according to the experimental groups. After 24 h, microshear bond testing was performed at 0.5 mm/min crosshead speed until the failure. Data were submitted to one-way ANOVA followed by Tukey test (p<0.05). Scanning electron microscopy (SEM) was used for classifying the failure modes. Results Higher DC and bond strength values were shown by the resin cements cured by using the dual activation mode. The Variolink II group presented higher DC and bond strength values when using light-activation only when compared with the Variolink Veneer group. Conclusion The base paste of dual-cured resin cements in light-activation mode can be used for bonding translucent ceramic restorations of up to or less than 1.0 mm thick.

Micro-computed tomographic evaluation of removal and extrusion of root filling material during canal retreatment / Avaliação por meio de microtomografia computadorizada da remoção e extrusão de material obturador durante retratamento endodôntico

This study aimed to assess the efficiency of manual and rotary techniques for removing root filling material in endodontic treated canals and to evaluate the extrusion of debris via apical foramen. After access preparation, thirty human lower central incisors were instrumented, filled and divided into two groups (n=15): MNmanual retreatment technique; RT- rotary retreatment technique. The teeth were submitted to micro-computed tomographic scanning before and after the retreatment procedure, for quantifying the remaining filling material by relating the initial and final conditions. The analysis was conducted separately in all root thirds. The volume of material extruded through the apical foramen was also quantified. The data were statistically analyzed using t-test and two-way analysis of variance (ANOVA) at 5% of significance. No significant differences were detected between remaining filling material for the techniques evaluated (p=0.74), even considering the apical third only (p>0.75). Significant differences were found for the remaining filling material verified between the cervical third and middle/apical thirds, with lower values being observed at the cervical third for both groups (p<0.05). Apical extrusion of filling material was verified in seven specimens (2 from MN group and 5 from RT group). Both techniques showed similar performance for removing filling material from the root canal, considering the whole tooth or the root thirds independently. The apical extrusion of filling material observed was not sufficient to indicate which technique has increased tendency to induce more events during retreatments.

Este estudo objetivou avaliar a eficiência das técnicas manual e rotatória na remoção de material obturador de dentes tratados endodonticamente, além de verificar a extrusão de resíduos via forame apical. Após acesso endodôntico, trinta incisivos centrais inferiores humanos foram instrumentados, obturados e divididos em dois grupos (n=15): MN- técnica de retratamento manual; RT- técnica de retratamento rotatória. Os dentes foram submetidos à escaneamento micro-tomográfico previamente e após os procedimentos de retratamento para quantificação do remanescente de material obturador relacionando as condições inicial e final. Esta análise foi conduzida separadamente em todos os terços radiculares. O volume de material extruído via forame apical também foi quantificado. Os dados foram analisados estatisticamente por meio dos Testes T e de Análise de Variância em dois níveis com significância em 5%. Diferenças significantes não foram detectadas entre a quantidade de material remanescente para as duas técnicas avaliadas (p=0,74), mesmo considerando o terço apical separadamente (p>0.75). Diferenças significantes foram encontradas na quantidade de material remanescente verificado entre os terços cervical e médio/apical, com menores valores detectados no terço cervical para ambos os grupos (p<0.05). Extrusão apical de material obturador foi identificada em sete espécimes (2 do grupo MN e 5 do grupo RT). As duas técnicas avaliadas apresentaram desempenho similar na remoção do material obturador do canal radicular, considerando o dente como um todo ou os terços radiculares separadamente. A extrusão apical de material obturador verificada não foi suficiente para indicar qual técnica possui maior tendência de promover eventos durante o retratamento.

Influence of flexion angle of files on the decentralization of oval canals during instrumentation.

The aim of this study was to evaluate the influence of the flexion angle of files on the decentralization of root canals during instrumentation. Fifteen lower incisors were instrumented with Protaper Universal files and radiographed in two directions (mesiodistal and buccolingual) before and after instrumentation with a #15 K-file in position for evaluating the flexion angle of files. The specimens were also scanned before and after instrumentation using micro-computed tomography to obtain the canal area and the distance from the center position of the file to the canal walls. Sections located 1.0 mm (end of the canal), 3.0 mm (apical third), 9.0 mm (middle third), and 15.0 mm (cervical third) from the apex were verified. After instrumentation, the flexion angles of files decreased by an average of 0.76º in the buccolingual direction and 1.92º in the mesiodistal direction (p < 0.001); the canal area increased by an average of 0.58, 0.37, 0.23 and 0.13 mm(2) from the cervical to the end of the root canal (p < 0.001). Non-instrumented areas were observed on the buccal and lingual walls, and effective action of files was determined on the mesial and distal walls. The sections from the end of the canal showed canal deviation toward the lingual wall, whereas the other sections showed deviation toward the buccal wall. The flexion angles of files influence the final shape of the root canal, resulting in file decentralization along the pathway of the canal.

Multidisciplinary treatment of congenitally missing maxillary lateral incisors: a case report / Tratamento multidisciplinar de agenesias de incisivos laterais superiors: relato de caso

Congenital tooth agenesis and tooth loss due to dental traumatism are some of the most common causes leading to rehabilitation of young patients with dental implants. The success of treating congenitally missing teeth with implant-supported prosthesis is no more guided only by osseointegration criteria. Nowadays the successful rehabilitation of these cases involves the adequate installation of dental implants with suitable prosthetic contour, color, and emergence profile closer to that found in natural dentition. Several treatment options are available for restoring patients with congenitally missing teeth such as maxillary lateral incisors. Fixed prosthodontics and orthodontics managements are considered acceptable treatment protocols. However, the gold standard rehabilitation of congenitally missing maxillary incisors is performed with implant-based prosthesis since no tooth wear neither extensive tooth movements are necessary. The present paper reports the treatment of a young adult woman with congenitally missing maxillary lateral incisors who underwent orthodontic treatment for improvement of teeth alignment and occlusal balance previous to dental implant surgery. This treatment also allowed appropriate space for the future lateral incisors crowns. Then, Morse-type conical implants were positioned and prosthetic abutments installed. Ceramic laminates were planned on central incisors in order to improve anterior aesthetics. All-ceramic crowns and laminates were made using lithium dissilicate-based ceramic (e-Max Press). The multidisciplinary association of orthodontic, implant and prosthetic techniques resulted in successful functional and aesthetic rehabilitation of the case, which was maintained after 1 year follow up.

Agenesias e perdas dentárias devido a traumatismos estão entre as principais causas de reabilitações de pacientes jovens com implantes dentários. O sucesso do tratamento de agenesias com implantes osseointegrados não se limita mais à osseointegração exclusivamente. Atualmente, o sucesso da reabilitação destes casos envolve a correta instalação de implantes que favoreçam a confecção de uma prótese com cor, forma e perfil de emergência o mais semelhante possível aos dentes naturais. Os cirurgiões-dentistas têm várias opções para tratar casos de agenesias como as de incisivos laterais superiores. Próteses fixas convencionais e movimentação ortodôntica são considerados protocolos de tratamento aceitáveis. Entretanto, agenesias de incisivos laterais superiores são reabilitadas satisfatoriamente com próteses sobre implantes uma vez que extensas movimentações ou desgastes dentários são necessários. O presente caso relata o tratamento de uma paciente jovem com agenesia dos incisivos laterais que havia feito tratamento ortodôntico para correção do posicionamento dentário e equilíbrio dental antes de se submeter à cirurgia para instalação de implantes. O tratamento ortodôntico também favoreceu a obtenção de espaço apropriado para instalação das coroas dos incisivos laterais. Posteriormente, implantes cônicos com plataforma protética tipo cone morse foram instalados e pilares selecionados. Laminados cerâmicos foram planejados para os incisivos centrais com objetivo de se promover um resultado final mais harmônico e estético. As coroas em cerâmica pura e laminados foram confeccionados com cerâmica a base de dissilicato de lítio (e.Max Press). A associação multidisciplinar entre tratamento ortodôntico, implantes e próteses sobre implantes resultou no sucesso funcional e estético da reabilitação do presente caso com acompanhamento clínico de uma ano.

Morphometric evaluation and planning of anticurvature filing in roots of maxillary and mandibular molars.

This study aimed to guide the planning of anticurvature filing using pre-determined anatomical points on teeth to establish directions for proper implementation of the technique. Two hundred digital periapical radiographs of human molar teeth were selected and divided into two groups (n = 100): MX (maxillary) and MD (mandibular) molars. Mesiobuccal roots were considered for the MX group and mesial roots for the MD group. Pre-determined anatomical points required for planning the anticurvature filing on the root canal path were located, and the distances between these points obtained. The anticurvature filing was simulated in two different protocols for each group, and the region of dentin removal and the remaining dentin thickness were measured in the safety and danger zones of the root canals. Statistical analysis was carried out at a significance level of 5%. The distances between the anatomical points and the thickness of remaining dentin showed significant differences when the two groups were compared (p < 0.001). No significant differences were found between the two experimental groups regarding the area of dentin removal at the root region, but differences were detected in comparison with dentin removal at the crown (p < 0.001). In terms of wear produced after simulation of both anticurvature filing protocols, significant differences were verified for all regions, except for the dentin remaining at the danger zone. The radiographic location of anatomical points allows for planning and implementation of controlled and efficient anticurvature filing and can be performed in the same manner for maxillary and mandibular molars.

Morphometric evaluation and planning of anticurvature filing in roots of maxillary and mandibular molars

This study aimed to guide the planning of anticurvature filing using pre-determined anatomical points on teeth to establish directions for proper implementation of the technique. Two hundred digital periapical radiographs of human molar teeth were selected and divided into two groups (n = 100): MX (maxillary) and MD (mandibular) molars. Mesiobuccal roots were considered for the MX group and mesial roots for the MD group. Pre-determined anatomical points required for planning the anticurvature filing on the root canal path were located, and the distances between these points obtained. The anticurvature filing was simulated in two different protocols for each group, and the region of dentin removal and the remaining dentin thickness were measured in the safety and danger zones of the root canals. Statistical analysis was carried out at a significance level of 5%. The distances between the anatomical points and the thickness of remaining dentin showed significant differences when the two groups were compared (p < 0.001). No significant differences were found between the two experimental groups regarding the area of dentin removal at the root region, but differences were detected in comparison with dentin removal at the crown (p < 0.001). In terms of wear produced after simulation of both anticurvature filing protocols, significant differences were verified for all regions, except for the dentin remaining at the danger zone. The radiographic location of anatomical points allows for planning and implementation of controlled and efficient anticurvature filing and can be performed in the same manner for maxillary and mandibular molars.

Influence of flexion angle of files on the decentralization of oval canals during instrumentation

The aim of this study was to evaluate the influence of the flexion angle of files on the decentralization of root canals during instrumentation. Fifteen lower incisors were instrumented with Protaper Universal files and radiographed in two directions (mesiodistal and buccolingual) before and after instrumentation with a #15 K-file in position for evaluating the flexion angle of files. The specimens were also scanned before and after instrumentation using micro-computed tomography to obtain the canal area and the distance from the center position of the file to the canal walls. Sections located 1.0 mm (end of the canal), 3.0 mm (apical third), 9.0 mm (middle third), and 15.0 mm (cervical third) from the apex were verified. After instrumentation, the flexion angles of files decreased by an average of 0.76º in the buccolingual direction and 1.92º in the mesiodistal direction (p < 0.001); the canal area increased by an average of 0.58, 0.37, 0.23 and 0.13 mm2 from the cervical to the end of the root canal (p < 0.001). Non-instrumented areas were observed on the buccal and lingual walls, and effective action of files was determined on the mesial and distal walls. The sections from the end of the canal showed canal deviation toward the lingual wall, whereas the other sections showed deviation toward the buccal wall. The flexion angles of files influence the final shape of the root canal, resulting in file decentralization along the pathway of the canal.

Critical instrumentation area: influence of root canal anatomy on the endodontic preparation.

The aim of this study was to evaluate the root canal anatomy of mandibular incisors before and after endodontic instrumentation, identifying regions inaccessible to the action of files (Critical instrumentation Area - CA) in a three-dimensional perspective. Thirty human mandibular central incisors were selected, assigned to two groups (n=15) and instrumented using ProTaper Universal rotary files. In the RX group, longitudinal digital radiographic images were obtained in the buccolingual (BL) and mesiodistal (MD) views. In the CT group, cross-sectional micro-computed tomography (µCT) images were obtained at 3, 9 and 15 mm from the apex. The canal area of the specimens was evaluated before and after instrumentation using digital images from each group. Data were analyzed using t-test, one-way ANOVA with subdivided parcels and Tukey's test (α=0.05). The canal area found in the MD radiographs was larger than in the BL radiographs, which was also confirmed in the transversal images (p<0.01). The CA was only detected in the MD radiographs and µCT scans. On the root canal configuration, a continuous reduction in the canal conicity was observed in BL radiographs, while in MD view there was a constriction at the cervical third and subsequent increase at the middle third (p<0.01). The conical shape of the root canal was observed only in the BL view. The canal enlargement in BL radiographs was not indicative of homogeneous instrumentation, since unprepared areas (CA) were also verified on the buccal and lingual walls in different images.